Silicone Rubber Curing Agent For Silicone Ice Mold for FDA level
Silicone Rubber Curing Agent For Silicone Ice Mold for FDA level
Silicone Rubber Curing Agent For Silicone Ice Mold for FDA level
Silicone Rubber Curing Agent For Silicone Ice Mold for FDA level
Silicone Rubber Curing Agent For Silicone Ice Mold for FDA level

Silicone Rubber Curing Agent For Silicone Ice Mold for FDA level

Model NO.:
PTC-100-1AB
Price:
USD 50.00-60.00 / ton
Delivery:
FOB
Minimum order quantity:
1 ton
Supply Ability:
10 ton / Week
Country of Origin:
Shenzhen
Quantity:
  • Classification:Catalyst
  • Place of Origin:CN;GUA
  • Application:Chemical Catalyst
  • Brand Name:KANGLIBANG
  • Model Number:PTC-100-1AB
  • Color:Milk white or semitransparent light yellow
  • Application:baby nipples, cake mold, silicone cookwares
  • Components:Two components
  • Warranty:4Months at room temperature without open.
  • Certificate:FDA ISO9001:2008
  • security level:Food and medical grade

Silicone Rubber Curing Agent For Silicone Ice Mold for FDA level

_.png

 

 

Good for both compression molding and extrusion forming.This agent are mainly applied to Food Grade and Medical Grade products, such as baby nipples, cake mold, silicone cookwares,extrusion gaskets ,ice mold, table matt, medical silicone tube and so on

 

feature_.png

 

PTC-100-1A& B,two component platinum addition type cross linking agent which is added in the raw silicones for the cross linking of food and medical grade silicone rubber items ,The vulcanized products can pass the FDA test,it features with non-toxic, odourless, high grade of transparency,well anti-yellowing and other properties.

 

 

_.png

 

Type one: Extrusion Or Injection Moulding

 

1.For High Tear Strength Silicone Materials (filled with gaseous phase white carbon black)

Application ratio:

 PTC-100-1B                          2.0~2.5%

 PTC-100-1A                          1.0~1.5%

 

Curing condition: IR(6meters),constant temperature ±5℃.

First curing: IR curing at 190~200℃ for40~60.

Finished curing: After first curing, it should be cured again as below conditions.

 

Curing temperature

155~165℃

165~175℃

Over175℃

Curing time

3~5minutes

3minutes

2minutes

 

2. For Normal Silicone Material

 

Application ratio:

PTC-100-1B                              2.0~2.5%

PTC-100-1A                              1.0~1.5%

Curing condition:IR(6meters),constant temperature ±5℃.

First curing: IR(Infrared Radiation) curing at 190~200℃ for40~60 seconds.

Finished curing:After first curing, it should be cured again as below conditions.

 

Curing temperature

80~90℃

95~110℃

115~135℃

Curing time

7 minutes

5 minutes

4 minutes

 

Type two: CompressionMolding 

 

 

PTC-100-1B                              2.0~2.5%

PTC-100-1A                              1.0-1.5%

Curing temperature: 115~135℃(200~300seconds)

Curing time:Can be adjusted with the thickness and type of the silicone products

 

 

.png

 

 

_.png

 

1.The raw material is easy poisoning once contact with nitrogen, phosphorus, sulfur and heavy metal materials.

2.Part A and Part B can not be added at the same time , addition of Part B comes first ,followed by part A after full incorporation of part B into raw silicones , the order is important, A and B can not be mixed together.

3. The temperature of mixing machine which used for mixing silicone with platinum curing agent can not be higher than 45℃. Please add this agent after being cold.

4. The mixed raw materials should be used up within two days.

5. Please choose the suitable raw materials for hot air vulcanization,unmatched raw material will cause bubbles in the process.

 

FAQ- C-100AB.png

 

 

packing_.png

 

1KG / Bottle

 

.png

 

 4months at room temperature without open.

 