- Place of Origin:CN;GUA
- Classification:Other Adhesives
- Model Number:KL-F6060AB
- Brand Name:kanglibang
- Type:Two Component
- Usage:Fiber & Garment
- Usage:Footwear & Leather
- Usage:Packing
- Main Raw Material:Silicone
- Appearance:A: Transparent gel B: Milky white gel
- Viscosity(mPa.s) GB-T 11409.8-1989:A: 4300000 B: 5500000
- Shore Hardness (A):60±2
- Tensile Strength(Mpa):≥7.0
- Tear strength(kN/m):≥25
- Elongation at break(%):≥300
- Curing condition:TC10: 120℃*42S-TC90:120℃*92S
- Specifical gravity(g/cm3):1.10±0.02

KL-F6060AB,Self adhesive LSR , is addition type LSR , It has strong bond to thermoplastics
like polycarbonate and does not stick to the mold featuring with fast curing speed .


Wireless chargers ,silicone precision electronic Baby products

Silicone cell phone cases Silicone medical products

1,Spare from use of base primer , bond to different substrates
2,Easily pigmentabel
3,Releasable from the metal mold
4,Short curing time
5,Suitable for silicone overmolding products , insert molding or double injection molding ,
partly needing bond and sophisticated precision parts.
6,Maximise the productivity and reduce labour costs
7,The finished product ok rate is highest






1, The tool used to take A and B should not be the same to avoid partial lumps. 2, The mixed A and B are reserved for three days, The higher the temperature , the shorter the
reservation time.
3, The LSR should be avoided contact with N,S,P and Sn, otherwise , it will cause curing failure
or insufficent curing.
4, The ideal mixing ratio would be 1:1,over inbalance of the mixing ratio will affect the properties
of the made silicone products